The Commit Group specializes in processing and marketing of galvanized steel in coils, strips and sheets to standard and custom sizes. These products consist of a steel substrate over which a coating of zinc is applied by continuous hot dipping. The percentage of zinc contained in the coating is more than 99%. The main characteristic of these products lies in the remarkable corrosion resistance offered by zinc depending on the thickness of the coating.
The maximum exposure temperature for this type of product is 200 °C.
Hot dipping enables a wide range of zinc thicknesses, including very high thicknesses of up to 725 g/m2 total on the two faces.
| Name | Type of coating | Yield strength | Rupture | Elongation | Plastic deformation ratio | Cracking | |
| Quality | Type of coating | Re MPag | Rm MPag | A80 % min | r90 min | n90 min | |
| DX51D | +Z, +ZF, +ZA, +ZM, +AZ, +AS | – | 270 to 500 | 22 | – | – | |
| DX52D | +Z, +ZF, +ZA, +ZM, +AZ, +AS | 140 to 300 | 270 to 420 | 26 | – | – | |
| DX53D | +Z, +ZF, +ZA, +ZM, +AZ, +AS | 140 to 260 | 270 to 380 | 30 | – | – | |
| DX54D | +Z, +ZA | 120 to 220 | 260 to 350 | 36 | 1,6 | 0,18 | |
| DX54D | +ZF, +ZM | 120 to 220 | 260 to 350 | 34 | 1,4 | 0,18 | |
| DX54D | +AZ | 120 to 220 | 260 to 350 | 36 | – | – | |
| DX54D | +AS | 120 to 220 | 260 to 350 | 34 | 1,4 | 0,18 | |
| DX55D | +AS | 140 to 240 | 270 to 370 | 30 | – | – | |
| DX56D | +Z, +ZA | 120 to 180 | 260 to 350 | 39 | 1,9 | 0,21 | |
| DX56D | +ZF, +ZM | 120 to 180 | 260 to 350 | 37 | 1,7 | 0,2 | |
| DX56D | +AZ, +AS | 120 to 180 | 260 to 350 | 39 | 1,7 | 0,2 | |
| DX57D | +Z, +ZA | 120 to 170 | 260 to 350 | 41 | 2,1 | 0,22 | |
| DX57D | +ZF, +ZM | 120 to 170 | 260 to 350 | 39 | 1,9 | 0,21 | |
| DX57D | +AS | 120 to 170 | 260 to 350 | 41 | 1,9 | 0,21 | |
| g 1MPa = 1N/mm2 | |||||||
| Coating name | Minimum weight1) | Typical values of coating thickness per side in the single spot test | Density | ||
| g/m2 | μm | ||||
| Triple spot test | Single spot test | Typical value | Range | ||
| Weight of the zinc (Z) coating | |||||
| Z100 | 100 | 85 | 7 | 5-12 | 7,1 |
| Z140 | 140 | 120 | 10 | 7-15 | |
| Z200 | 200 | 170 | 14 | 10-20 | |
| Z225 | 225 | 195 | 16 | 11-22 | |
| Z275 | 275 | 235 | 20 | 15-27 | |
| Z350 | 350 | 300 | 25 | 19-33 | |
| Z450 | 450 | 385 | 32 | 24-42 | |
| Z600 | 600 | 510 | 42 | 32-55 | |
| 1) The g/m2 include both surfaces | |||||
N | NORMAL: consists of large regular and bright grains |
M | MICROGRAIN: has small grains, in some cases not visible to the naked eye, due to antimony content and controlled cooling |
A | Minor imperfections - such as small honeycombs, variations in grain size, dark spots, light scratches, and passivation spots - are possible |
B | It is obtained through skinpass. Small imperfections - such as scratches due to skinpass, streaks, irregularities (not cavities) - are possible with this kind of surface |
C | It is obtained through skinpass. The best surface does not harm the apparent uniformity of a high color finish class; the other surface must be at least type B |
C | Chemical passivation, traditionally chromium-based; also available free of trivalent chromium, in compliance with the RoHS Directive; greenish residues may remain on the surface that do not alter product characteristics |
O | Oiling using oils that can be removed during greasing without compromising the coating |
CO | Combination of oiling and chemical passivation to enhance the protective effect against corrosion |
S | Organic passivation, commercially referred to as AFP (Anti Finger Print) or SPT (Resin Coating), consisting of a polymer film containing corrosion inhibitors; available free of hexavalent chromium; improves corrosion protection, prevents fingerprinting, facilitates sliding during processing, and acts as a primer during painting |
P | Phosphating, particularly suitable for the application of a subsequent layer of paint |
PO | Combination of phosphating and oiling to improve formability |
U | Without any protection, under the customer’s responsibility |
• Air conditioning
• Refrigeration
• Cars
• Poultry
• Dryers
• Elevators
• Household appliances
They can be supplied with special requirements for coating finish, surface appearance and surface protection.
The size and appearance of the grain, as well as its brilliance, do not affect the quality of the coating; however, if you require a particular size or shine requirement for the grain, it is imperative to specify this when ordering.
The surface appearance can be type A, B or C; unless otherwise requested at the time of order, the material is supplied with appearance A.
Surface protection can be of different types and must be appropriately indicated when placing the order.
Whatever the type of protection, it is very important that during transportation and storage, galvanized materials avoid contact with moisture or water as much as possible and are kept in a dry environment.
Commit Siderurgica SPA
Via dell’industria, 23
35030 Veggiano (PD)
VAT no. 01958150284
Commit Metalli SRL
Via volta, 69
35030 Veggiano (PD)
VAT no. 04678270283